High Transparency PC Film

Price:
Negotiable
minimum:
Total supply:
Delivery term:
The date of payment from buyers deliver within days
seat:
Guangdong
Validity to:
Long-term effective
Last update:
2022-08-30 07:29
Browse the number:
68

Send an inquiries

Company Profile

Tesei New Materials (Dongguan) Co., Ltd

By certification [File Integrity]

Contact：dechengxcl(Mr.)

Email：

Telephone：

Phone：

Area：Guangdong

Address：Guangdong

Website：http://www.teseidg.com/ http://dechengxcl.cnhaofan.com/

Product Details

Description

Our High Transparency PC Films effectively provide high temperature resistance, excellent dimensional stability, and good printability without pretreatment, and are suitable for a wide range of applications such as overlays, labels and in-mold decoration. And they can also be screen printed with a variety of inks, with impressive stiffness and tough material. They are not easily damaged even when used outdoors, and their good electrical insulating properties and excellent printability allow them to be reused in various fields.

Features

Our High Transparency PC Film is a transparent general purpose film from the thermoplastic polymer range, they can be used in thermoforming and forming techniques and are easy to die-cut. They also have excellent ink adhesion and can be printed with high contrast and clarity, combining images and text. They are high-technology treated so that they never stick to each other even when stacked together, solving the problem of long-term storage.

Details

Type	OM81	OM82	OM11
Thickness (mm)	0.125~6.0	0.125~6.0	0.05~6.0
Protective film	Double coated	Double coated	Double coated
Function and color	Single-sided hardening, high transparency	Double sided hardening, high transparency	Double sided polished, high transparency
Picture

Item	Property	OM81	OM82	OM11	Unit	Test Method
Optical Properties	Haze	<0.5	<0.5	<0.5	%	ASTM D1003
Physical Properties	Density	1.2	1.2	1.2	g/cm³	ISO 1183
	Pencil Hardness	HB~H	HB~H	HB~H	1000g	ASTM D3363
	Abrasion Resistance	No Damage	No Damage	-	0000# steel wool, with 250g/cm² pressure, 5cm stroke reciprocating 25 times	-
	Hot Water Resistance	No Change	No Change	-	80℃（hot water）×10min	-
	Moisture Resistance	No Change	No Change	-	70℃×80%RH×48h	-
	Heat Resistance	No Change	No Change	-	80℃×40min	-
	Low Temperature Resistance	No Change	No Change	-	-30℃×10h	-
	Cold & Heat Cycle Test	No Change	No Change	-	-30℃×6h←→23℃×3h （10 cycles）	-
	Adhesion	No Detaching	No Detaching	-	Cross-hatching test	-
Mechanical	Tensile Strength	60	60	-	-	ISO 527
Properties	Flexural Strength	85	85	-	-	ISO 178
Chemical Resistance	Ethanol Resistance	No Change	No Change	-	Coated sample hardening layer wiped with absorbent cotton ball fully immersed in test solution, then sealed with PE film, left at room temperature for 24 h, rinsed with pure water, then observation	-
	Weak Acid Resistance（0.5%）	No Change	No Change	-		-
	Salt Water Resistance 5%	No Change	No Change	-		-
Flammability		V-2/VTM-2	E249605

Physical Parameters：

Tip: This test is for reference only, not for absolute indicator of application.

Certification：

Product Application：

http://www.teseidg.com/